대한치과재료학회지 2020년 47권 3호 p.119 ~ 130
오현진, 최고운, 이창하, 임범수, 이인복,
소속 상세정보
오현진 ( Oh Hyun-Jin ) - Seoul National University School of Dentistry Department of Conservative Dentistry
최고운 ( Choi Go-Woon ) - Seoul National University School of Dentistry Department of Conservative Dentistry
이창하 ( Lee Chang-Ha ) - Seoul National University Dental Hospital One-Stop Specialty Center
임범수 ( Lim Bum-Soon ) - Seoul National University School of Dentistry Department of Dental Biomaterials Science
이인복 ( Lee In-Bog ) - Seoul National University School of Dentistry Department of Conservative Dentistry

Abstract

본 연구는 복합레진의 광중합 전과 후의 투과도 변화를 실시간으로 측정하여 복합레진의 색상 및 두께에 따른 변화를 관찰하고자 하였다. 펄스 폭 변조(pulse width modulation) 광조사기를 이용해 실시간으로 복합레진의 투과도를 측정할 수 있는 장치를 제작하여 실험에 이용하였으며, 미세혼합형 Filtek Z250 복합레진의5가지 색상(A1, A2, A3, A3.5, A4)에 따른 투과도와 4가지 두께(0.16, 0.50, 1.0, 1.5 mm)에 따른 투과도를 실시간으로 측정하였다. 투과도 변화율의 최대값과 peak time으로 중합역학을 관찰하였고, 중합 전과 후의 감쇠상수를 비교하였다. 중합 후 모든 시편에서 투과도가 증가했다. 색상에 따라서는 중합 전후 모두 A2가 최고, A1이 최저 투과도를 나타냈다. 중합 전 후 투과도 변화와 최대 변화율은 A2가 최고, A3.5가 최저였으며, peak time은 3.10~4.07초로 색상별로 유의한 차이는 없었다. 시편이 얇아질수록 투과도와 투과도 변화율 모두 증가했으며, peak time은 1.5 mm 두께에서 최대였다. 감쇠상수의 절대값은 모든 시편에서 중합 후에 감소했다. 결론적으로 복합레진은 중합 후 투과도가 증가하는데 색상에 따라 중합 전과 후의 투과도는 모두 다른 값을 보였고, 두께가 얇을수록 투과도가 증가하였다. 시간에 따른 투과도 변화율을 통해 중합역학 또한 관찰할 수 있었다.

The purpose of this study was to measure the transmittance change of composites during light curing in real time according to different shades and thicknesses. An instrument using pulse width modulation-curing light was developed to measure the transmittance of composites in real time. A micro-hybrid composite, Filtek Z250, was used for %transmittance measurement with five different shades (A1, A2, A3, A3.5, A4) and 4 different thicknesses (0.16, 0.5, 1.0, 1.5 mm). The maximum value of d (%Transmittance)/ d t and peak time were used to observe polymerization kinetics. Attenuation coefficient was also compared between pre and post cured specimens. The transmittance increased in all specimens after polymerization. A2 showed the highest and A1 showed the lowest transmittance in both pre and post curing. The transmittance change and maximum rate of change were highest in A2 and lowest in A3.5, and the peak time, which ranged in 3.10 to 4.07, was not significantly different among shades. As the specimen became thinner, both the transmittance and rate of change increased, and the peak time was maximum at 1.5 mm thickness. The absolute value of attenuation coefficient decreased after polymerization in all specimens. In conclusion, the transmittance of composite increased after polymerization. Each shade showed different transmittance value for both pre and post curing state, and thinner specimen showed higher transmittance value. Polymerization kinetics could also be observed through the rate of transmittance change over time.

키워드

감쇠계수; 복합레진; 투과도; 광중합; 중합역학
Attenuation coefficient; Composites; Light curing; Polymerization kinetics; Transmittance