나노 크기 수산화인회석과 삼인산칼슘을 첨가한 실험용 불소바니쉬의 재광화 효과

Remineralization effect of experimental fluoride varnish with nano-sized hydroxyapatite and tricalcium phosphate

대한치과재료학회지 2020년 47권 3호 p.131 ~ 142
신성진, 손주리, 오승한, 배지명,
소속 상세정보
신성진 ( Shin Seong-JIn ) - Wonkwang University College of Dentistry Department of Dental Biomaterials
손주리 ( Son Ju-Lee ) - Wonkwang Health Science University Department of Dental Hygiene
오승한 ( Oh Seung-Han ) - Wonkwang University College of Dentistry Department of Dental Biomaterials
배지명 ( Bae Ji-Myung ) - Wonkwang University College of Dentistry Department of Dental Biomaterials

Abstract

이 실험의 목적은 불소바니쉬 단독과, 불소바니쉬에 나노 크기의 수산화인회석과 나노크기의 삼인산칼슘을 첨가한 후, 탈회/재광화 사이클링 하에서 재광화 정도를 비커스 경도로 평가하는 것이다. 불화나트륨 5 wt%를 함유한 로진제재의 실험용 불소바니쉬를 제작하였다(EX). 실험용 불소바니쉬에 나노 수산화인회석(HA+EX)과 나노 삼인산칼슘(TC+EX)을 각각 10 wt%씩 넣어 제작하였다. 기성품인Casein phosphopeptide-amorphous calcium phosphate (CP: Tooth mousse, GC, Japan)는 비교를 위해 사용되었다. 대조군은 아무런 처리도 하지 않았다. 우치 전치부를 아크릴릭 레진에 포매한 후 우식유발 용액에 72시간 노출시킨 후, EX, HA+EX, TC+EX, CP를 시편에 도포하였다. 탈회/재광화 사이클은 각각1시간 /23시간으로 구성되었고, 20일까지 반복하였다. 재광화 정도를 평가하기 위해 시험 전과 각 처치 후 비커스 경도를 측정하였다. 각 군의 재료들을 도포한 지 24시간 후 CP군이 가장 높은 경도값을 보였고(p<0.05), 다른 군들은 통계적으로 유의한 차이가 없었다(p>0.05). 탈회/재광화 사이클링 10일 후, TC+EX군이 가장 높은 경도값을 보였지만(p<0.05) HA+EX군과는 차이가 없었다(p>0.05). 탈회/재광화 사이클링 20일 후, TC+EX군은 가장 높은 경도값을 보였고, HA+EX군 과 EX군이 그 다음으로 높았다(p<0.05). 결론적으로10 wt%의 나노 삼인산칼슘이 첨가된 실험용 불소바니쉬 군이 탈회/재광화 사이클하에서 법랑질을 가장 효과적으로 재광화시켰다.

The purpose of this study was to evaluate the remineralization effect of experimental fluoride varnish mixed with nano-tricalcium phosphate (TCP) and nano-hydroxyapatite (HA) on bovine teeth under demineralization and remineralization cycling by Vickers hardness. After fabrication of rosin-based experimental fluoride varnish with 5 wt% of NaF (EX) in the laboratory, 10 wt% of nano-hydroxyapatite (HA+EX) and nano-TCP (TC+EX) were mixed, respectively. Casein phosphopeptide-amorphous calcium phosphate (Tooth mousse) (CP) was used for comparison. Bovine incisors were impregnated by acrylic resin and exposed to caries inducing solution for 72 hours. EX, HA+EX, TC+EX, and CP were applied on the surface of bovine teeth. The specimens were immersed in a demineralization solution for 1 hour and in a re-mineralization solution for 23 hours and the cycle was repeated for 20 days. Vickers hardness was measured at baseline and after each treatment. CP group showed the highest hardness value at 24 hours after application of each material (p<0.05) and the other groups were not significantly different (p>0.05). On the 10th day of de-/re-mineralization cycling, the TC+EX group showed the highest hardness value (p<0.05), but not significantly different from the HA+EX group (p>0.05). On the 20th day, the TC+EX group kept the highest hardness value, followed by HA+EX and EX groups (p<0.05). In conclusion, experimental fluoride varnish with 10 wt% of nano-TCP showed higher remineralization effect on the enamel of bovine teeth during the de/re-mineralization cycling.

키워드

재광화; 탈회; 수산화인회석; 삼인산칼슘; 비커스 경도; 불소바니쉬
Remineralization; Demineralization; Hydroxyapatite; Tricalcium phosphate; Vickers hardness; Fluoride varnish